High Strength And Conductivity Annealed (A or TB00) CuBe2 Copper Strips For Bearings
Product Normal Description:
Product Name: High strength and conductivity copper strips
Grade: CuBe2
Standard: ASTM B194, SAE J463, J461
Product Specification: 0.1mm-0.5mm
State: Annealed (A or TB00)
Typical Application: used for bearings
Product Brand: CUBERYLLIUM®
Chemical Composition of CuBe2 Copper Alloy (CUBERYLLIUM ®-172):
Product Grade: CUBERYLLIUM ®-172(UNS. C17200)
Beryllium(Be): 1.80-2.00%
Cobalt(Co) + Nickel(Ni): 0.20% Min
Cobalt(Co) + Nickel(Ni) + Iron(Fe): 0.60% Max
Lead: 0.02% Max
Copper(Cu): Balance
Note: Copper plus additions equal 99.5% Minimum.
Typical Physical Properties of CuBe2 Copper Alloy(CUBERYLLIUM ®-172):
| Density (g/cm3): | 8.36 |
| Density before age hardening (g/cm3): | 8.25 |
| Elastic Modulus (kg/mm2 (103)): | 13.4 |
| Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C): | 17 x 10-6 |
| Thermal Conductivity (cal/(cm-s-°C)): | 0.25 |
| Melting Range (°C): | 870-980 |
Temper Designations of CuBe2 Copper Strip(CUBERYLLIUM ®-172):
| Cuberyllium Designation | ASTM | Mechanical and Electrical Properties of Copper Beryllium Strip |
| Designation | Description | Tensile Strength
(Mpa) | Yield Strength 0.2% offset | Elongation Percent | HARDNESS
(HV) | HARDNESS
Rockwell
B or C Scale | Electrical Conductivity
(% IACS) |
| A | TB00 | Solution Annealed | 410～530 | 190～380 | 35~60 | <130 | 45~78HRB | 15～19 |
| 1/2 H | TD02 | Half Hard | 580～690 | 510～660 | 12~30 | 180~220 | 88~96HRB | 15～19 |
| H | TD04 | Hard | 680~830 | 620~800 | 2~18 | 220~240 | 96~102HRB | 15～19 |
| HM | TM04 |
Mill hardened | 930～1040 | 750～940 | 9～20 | 270～325 | 28～35HRC | 17～28 |
| SHM | TM05 | 1030～1110 | 860～970 | 9～18 | 295～350 | 31～37HRC | 17～28 |
| XHM | TM06 | 1060～1210 | 930～1180 | 4～15 | 300～360 | 32～38HRC | 17～28 |
| The Fabrication Properties of CuBe2 (C17200) Copper Alloys |
| Hot Working | |
| Cold Working | |
| Annealing | |
| Other fabrication properties | - Include blanking, drawing, drilling, forming and bending, tapping, and turning.
|
Applications of UNS.C17200 Beryllium Copper Alloy(CUBERYLLIUM ®-172):
CUBERYLLIUM ®-172 is usually used for electrical industry, fasteners and industrial.
Electrical Industry: electrical switch and relay blades(switch parts, relay parts), clips, fuse clips, connectors, spring connectors, navigational indstruments, contact bridges, belleville washers;
Fasteners: washers, lock washers, fasteners, retaining rings, roll pins, screws, bolts;
Industrial: pump parts, springs, electrochemical, spline shafts, non sparking safety tools, flexible metal hose, housings for indtruments, bearings, bushings, valve seats, valve stems, disphragms, springs, welding equipment, rolling mill parts, valves, bourdon tubes, wear plates on heavy equipment, bellows.
Product Photos:
FAQ:
Q1:Could you produce Beryllium Copper strip by Mill Hardened process.
A1:Yes, we could produce AM(TM00), 1/2HM(TM01).HM(TM04) XHM(TM06) XHMS(TM08).,we are the only factory could do harden strip in China.
Q2: What’s the advantages the Beryllium Copper of CUBERYLLIUM®.
A2: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous Furnace.
3:Surface further polishing for top clients.
Q3: Why you melting by Vacuum semi-Continuous Furnace.
A3:Could be get the Cast ingot without gas,smaller segregation, Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.
Product Tags:
|
|
Astm B196 A TB00 Annealed CuBe2 Copper Strips For Bearings High Strength Conductivity Images
|